O le paluina tui paluina shrinkage o se tasi o meatotino pe a paʻu le mea vevela paʻu. Le fua faatatau o tui suia suia shrankage i le fuafuaina o le mulimuli workpiece fua. O le tau e faʻailoa mai ai le aofaʻi o le faʻaitiitia na faʻaalia e se mea faigaluega ina ua maeʻa ona aveʻese mai le mamanu ona faʻamaaliliina lea i le 23C mo se vaitaimi e 48 itula.

O le Shrinkage e fuafuaina e le faʻatusatusaga lenei:

S = (Lm-Lf) / Lf * 100%

O le S o le fua o le faʻaitiitia o le suia, Lr o le mulimuli mea faigaluega (i. poʻo le mm), ma Lm le suia vaega foafoaina (i po o mm). O le ituaiga ma faʻavasegaina o mea palasitika ei ai fesuiaʻiga taua o shrinkage. E mafai ona aʻafia le faʻafefeteina e le tele o fesuiaʻiga e pei o le faʻamaluluina o le mamafa o mea faigaluega, tuiina ma le faʻatonutonuina o omiga. O le faʻaopopoina o mea e faʻatumu ma faʻamalosi tino, e pei o le tioata fiber poʻo le mineral filler, e mafai ona faʻaititia ai le faʻaitiitia.

O le faʻamamaina o oloa tau palasitika pe a maeʻa ona gaosi e masani, ae o le crystalline ma le amorphous polymers e faʻasolosolo eseese. O mea faigaluega uma palasitika e faʻamamaina pe a maeʻa ona faʻagasolo ona o se taunuuga o le latou mafai ona faʻatonutonu ma le faʻapipiʻi o le vevela a o latou maalili mai le gaosiga o le vevela.

Amorphous meafaitino maualalo shrinkage. Pe a faʻamaluluina mea e leai se aoga i le taimi e faʻamalulu ai le tuiina, latou te toe faʻasolosolo lelei i se plymer maumaututū. O filifili polymer e fausiaina ai le amorphous mea e leai se faʻatulagaina faʻapitoa. Faʻataʻitaʻiga pf amorphous mea o polycarbonate, ABS, ma polystyrene.

O mea crystalling material o loʻo i ai se faʻamatalaga faʻamaʻapeʻapeina tioata crystalline liu O filifili polymer faʻatulagaina latou lava i le faʻatonuina o le molelaa faʻatulagaina. Nei oka vaega o tioata e fausia pe a faʻamaluluina le polymer mai lona tulaga liusuavai. Mo semicrystalline polymer mea, o le faʻavaeina ma le faʻateleina o le teuina o filifili mole i nei vaega tioata. o le tui iniseti tipiina mo semicrystalline mea e maualuga atu nai lo amorphous mea. Faʻataʻitaʻiga o mea tioata o le nylon, polypropylene, ma le polyethylene. O loʻo lisiina atu ai le tele o mea palasitika, e le gata i le amorphous ma le semicrystalline, ma a latou suia tuumuli.

Tuumuli mo thermoplastics /%
meafaitino suia mumu meafaitino  suia mumu meafaitino suia mumu
ABS 0.4-0.7 polycarbonate 0.5-0.7 PPO 0.5-0.7
Acrylic 0.2-1.0 PC-ABS 0.5-0.7 polystyrene 0.4-0.8
ABS-nylon 1.0-1.2 PC-PBT 0.8-1.0 Polysulfone 0.1-0.3
Acetal 2.0-3.5 PC-fagafao 0.8-1.0 PBT 1.7-2.3
Nylon 6 0.7-1.5 Polyethylene 1.0-3.0 PET 1.7-2.3
Nylon 6,6 1.0-2.5 Polypropylene 0.8-3.0 TPO 1.2-1.6
PEI 0.5-0.7        

O le fesuiaʻiga o le faʻaitiitia o le aoga o lona uiga o le faʻagasologa o faapalepale mafai ona ausia mo amorphous polymers e sili mamao atu nai lo na mo crystalline polymers, aua o crystallites o loʻo sili atu ona okaina ma sili atu le teuina o polymer chain, vaega suiga faʻateleina shrinkage tele. Ae o palasitika e leai ni vai, ua naʻo le pau lea o le mea ma e faigofie ona fuafua.

Mo amorphous polymers, shrinkage aoga e le gata maualalo, ae shrinkage lava e vave ona tupu. Mo se masani amorphous polymer pei o le PMMA, o le shrinkage o le a i le faʻasologa o le 1-5mm / m. E mafua ona o le malulu mai pe tusa o le 150 (o le vevela o le liusuavai) i le 23C (potu vevela) ma mafai ona fesoʻotaʻi i le coefficient o le faʻalauteleina o le vevela.